Size compositions for glass fiber reinforced cementitious products

ABSTRACT

Acrylate-vinyl acetate copolymer size compositions for glass fiber reinforced cementitious products are disclosed. These size compositions show strong improvements in all phases of strand integrity with improved run-out performance in chopping.

This invention relates to a sizing composition. In one of its more specific aspects, this invention relates to a sizing composition for glass fibers which are incorporated into a cementitious matrix.

It has long been known, as described in Slayter U.S. Pat. Nos. 2,703,762 and 2,781,274, to employ glass fibers in the reinforcement of cementitious products, including hydrous calcium silicate crystals, cement, concrete, mortar, and like matrices having a high alkali content. Glass fiber reinforcement contributes significantly to the overall strength of such cementitious products by reason of the high strength and flexibility of the glass fibers.

Until the last decade, it has not been advisable to use glass fibers for long term (five or more years) reinforcement of cement, concrete, mortar, or other cementitious materials or matrices that have a high alkali content. The harsh alkali environment would degrade the types of glass fibers, E glass for example, commonly used to reinforce non-alkali materials such as plastics.

In more recent years, alkali-resistant glass fibers have achieved widespread acceptance. Such alkali-resistant glass fibers are described in U.S. Pat. Nos. 3,840,379; 3,861,927; and 3,861,926. It is now generally recognized that glass fibers formed from glass as described in such patents have significantly greater alkali rsistance than other conventional glass fibers, such as "E" glass fibers which have been in commercial use for some time and are described in U.S. Pat. No. 2,334,961.

Present sizes for alkali-resistant glass fibers for concrete and motor reinforcement have a performance history which is less than satisfactory. At times, the properties of conventional strands appear good. At other times, however, there is an overall non-uniformity in properties. When the properties drop to the lower extremes, they become very inadequate.

One problem appears to be strand integrity. If the integrity of the strand is somewhat low for the application being considered, excessive filamentation of the strand results which in turn reduces the workability of the cementitious mix to undesirable levels. Run-out of the strand from the forming package also may be a problem. In conventional sized strands, break-outs seem to occur more often than is desired during chopping. Both strand integrity and run-out are related. Usually, one can be improved at the expense of the other.

When strand integrity is low, problems of extensive filamentation occur in dry blending the glass with a cement matrix, as well as in wet mixes. The filamentation gives processing problems usually described as a reduced workability for wet mixes. A tough sizing, however, which bonds filaments together effectively within a strand to give high integrity, also will bond the whole strand strongly to the package. Thus, integrity is limited by the requirement of good run-out unless processing changes are made which allow integrity to be developed after run-out has been completed as in a damp chop operation followed by drying, or by eliminating the run-out altogether as in a wet chop operation at the bushing followed by drying.

We have discovered acrylate-vinyl acetate size compositions that yield a sized strand for glass fiber reinforced cement and concrete applications that is by far superior to other sized strands. The size compositions of this invention show strong improvement in all phases of strand integrity with improved performance in run-out in chopping. The dry integrity of strands sized with these compositions is especially good.

The size composition of this invention includes a copolymer of vinyl acetate and a long chain acrylate. The repeating unit of the vinyl acetate is ##STR1## i.e., --CH₂ CH(OOCCH₃)- and the repeating unit of the long chain acrylate is ##STR2## i.e., --CH₂ -CH(COOR)-- wherein R is hydrogen or an alkyl group containing 1 to 12 carbon atoms. Preferably R is an alkyl group containing 2 to 8 carbon atoms. The copolymer contains from 5 to 60% by weight of the acrylate. Preferably the weight percent of the acrylate is 15 to 35%. The balance of the copolymer is vinyl acetate. The molecular weight of the copolymer may vary from 20,000 to 150,000. Preferably the molecular weight is 30,000 to 80,000.

In addition to the foregoing, the aqueous size of this invention can include a silane such as vinyl-tri (beta-methoxyethoxy) silane or gamma-aminopropyltriethoxy silane, an acid such as glacial acetic acid, lubricants, surfactants, and the like.

The amount added of each material generally is of the order of 0.05 5% of the size composition. Ten to 30% of the size composition, preferably 15 to 25%, will be the acrylate-vinyl acetate copolymer.

The size of this invention can be applied to a single filament or to a multiplicity of filaments in any suitable manner. Preferably, it will be applied to a plurality of filaments from a conventional applicator, the filaments being collected into a roving package which is oven dried at about 265° F. The oven dried forming stock is then fabricated into roving packages comprising glass filaments having adhered to their surface a solid formed by the evaporation of the aqueous portion of the size, the solids comprising about 1.4-2.5 weight percent of the total strand weight, with 1.8-2.1 weight percent solids being preferred. In this respect, it is important to note that for best performance of the size of this invention, the strand solids is determinative rather than the solids content of the size.

While the size of this invention can be applied to any glass fibers, it is well adapted to glass filaments having diameters less than 0.001 inch.

In a broad sense, the glass fibers of this invention can be any well-known glass fiber or alkali-resistant glass fiber although the preferred form of this invention uses alkali-resistant glass fibers. Alkali-resistant glass fibers are now well known to those skilled in the art and are commercially available. In general, the glass from which alkali-resistant glass fibers are formed contains relatively high levels of zirconia, usually in amounts of the order of 5-25%. Most alkali-resistant glass fibers are:

    ______________________________________                                                             Parts by Weight                                            ______________________________________                                         SiO.sub.2             55-80%                                                   Alkaline earth metal oxide(s)                                                                        4-20%                                                    (CaO, MgO, BaO, etc.)                                                          Alkali metal oxide(s) 1-20%                                                    (Na.sub.2 O, K.sub.2 O, etc.)                                                  ZrO.sub.2             5-25%                                                    TiO.sub.2             O-10%                                                    ______________________________________                                    

In addition, these alkali-resistant glasses may also contain amounts of alumina, chromium oxide, tin oxide, and the like. Such alkali-resistant glass fibers are described in U.S. Pat. No. 3,840,379; 3,861,927; and 3,861,926.

There are many other well-known glass fibers that are commercially available. The most widely known of these are "E" glass fibers, which are described in U.S. Pat. No. 2,334,961 issued on Nov. 23, 1943.

The size composition of this invention will impart high strand integrity (high filamentation resistance) to the strands. The high integrity leads to more workable cementitious mixes where the strand may be mixed longer without excessive filamentation.

Strands of glass fibers are produced by pulling several hundred or more tiny molten streams of glass which issue from holes in the bottom of a molten glass tank over a size applying apron to a gathering shoe which groups the fibers together into a strand. This strand then proceeds to a traverse mechanism and winding drum which provides the pulling action which attenuates the molten glass and coils the strand into a package. The fibers are individually separated at the time that they pass over the size applicator, so that the surfaces of the fibers are substantially completely coated before they are drawn together into a strand.

While the term "glass fibers" is employed to define continuous glass fibers in the form of filaments, strands, yarns, bundles, and cords, it is also intended to include discontinuous fibers in the form of glass wool fibers and yarns and fibers of the continuous or discontinuous types which have been cut, chopped, or otherwise reduced to shorter lengths but preferably to lengths greater than 1/4 inch. Included also are the crimped continuous or discontinuous fibers or strands, yarns, and threads formed of the combination of crimped or uncrimped continuous and discontinuous fibers and fibrous bundles which have been plied or twisted in multiple groups to form yarns and cords.

While the preferred length of the glass fibers we employ in this invention ranges from 1/4 to 2 inches, we do not intend to exclude the use of continuous glass fibers. The total amount of fibers employed ranges from 1 to 40% by weight of cementitious material. Preferably, the total amount of fiber ranges from 2 to 25%.

Pulverizing naturally occurring hydraulic calcium silicate clinker produces hydraulic cement. The clinker generally includes silica, alumina, lime, iron oxide, and magnesia. The resulting powder hardens when mixed with water. Hydraulic cements include Portland, calcium-aluminate, magnesia, natural, masonry, pozzolana, and slag cements.

In many applications, fibers are combined with cementitious materials in accordance with known techniques such as the use of a spray gun in which the fibers are chopped, combined with cement, and sprayed onto a surface to form the glass fiber reinforced cementitious product.

If desired, it is believed possible to use other fibrous materials in addition to the sized glass fibers of this invention. These include asbestos fibers, mineral wool, and organic fibers such as wood pulp.

All fibers, whether employed in the form of continuous or chopped strands, are distributed throughout the cementitious material whereby the cementitious material forms a continuous phase with the fibers distributed and randomly dispersed throughout the cementitious materials in a discontinuous phase.

Having described the basic concepts of the invention, reference is now made to the following example which is provided by way of illustration, and not by way of limitation, of the practice of the invention in the manufacture of reinforced cementitious products made with the blends of this invention.

EXAMPLE I

An alkali-resistant glass having the following composition:

    ______________________________________                                         Ingredient         Weight Percent                                              ______________________________________                                         SiO.sub.2          61.1                                                        CaO                5.1                                                         Na.sub.2 O         14.4                                                        K.sub.2 O          2.6                                                         ZrO.sub.2          10.4                                                        TiO.sub.2          6.0                                                         Al.sub.2 O.sub.3   0.3                                                         Fe.sub.2 O.sub.3   0.2                                                         ______________________________________                                    

is formed into glass fibers using conventional techniques.

The fibers were made by drawing molten glass from a bushing having 204 orifices therein into individual fibers having a diameter of approximately 0.00055 inch. These individual fibers were coated with an aqueous solution of the following size and were gathered into a strand that was coiled into a package and dried:

    ______________________________________                                         Ingredient             Weight Percent                                          ______________________________________                                         copolymer of vinyl acetate and                                                                        20.0                                                    a long chain acrylate, Gelva                                                   Emulsion TS 100                                                                gamma-aminopropyltriethoxy silane,                                                                    1.0                                                     A-1100                                                                         glacial acetic acid    0.3                                                     aqueous emulsion of a tertiary                                                                        1.0                                                     amine, Protamine 65-20                                                         water, deionized       balance                                                 ______________________________________                                           Gelva Emulsion TS 100 has a vinyl acetate repeating unit of --CH.sub.2      CH(OOCCH.sub.3)-- and an acrylate repeating unit of --CH.sub.2 CH(COOR)--      wherein R is an alkyl radical containing 2 to 8 carbon atoms. Gelva 100      contains 20 to 30 weight percent of the acrylate, 70 to 80 percent vinyl      acetate, and has a molecular weight of about 50,000.

We also coated some of these same glass fibers in a similar manner with the following control size composition.

    ______________________________________                                         Ingredient               Weight Percent                                        ______________________________________                                         caprylic acid-tetraethylene pentamine                                                                   0.1                                                   condensate solubilized with acetic acid,                                       Cirrasol 185AN                                                                 Pelargonic acid-tetraethylene pentamine                                                                 0.2                                                   condensate solubilized with acetic acid,                                       Cirrasol 185AE                                                                 polyethylene glycol, Carbowax 100                                                                       0.2                                                   gamma-aminopropyltriethoxy silane, A-1100                                                               1.0                                                   polyvinylacetate plasticized with dibutyl                                                               12.9                                                  phthalate, 25-1048                                                             glacial acetic acid      1.2                                                   water, deionized         balance                                               ______________________________________                                    

The control size is the best conventional size for glass fiber reinforced cementitious products of which we are aware. A summary is given in Table I, where zero (0) represents no significant change from the control, plus (+) represents improvement and minus (-) represents a loss in property.

                                      TABLE I                                      __________________________________________________________________________     STRAND PROPERTY CHANGES                                                                 Strand                                                                         Solids                Chemical                                                                             Workability                                                                           Integrity of                                                                          Concrete                                                                               Run-                         (%) Wet Integrity                                                                           Dry Integrity                                                                           Resistance                                                                           of mix Strand Properties                                                                             Out                 __________________________________________________________________________     Control  2.0 0        0        0     0      0      0       0                   AVA      1.9 +        +++      +     +      +      0       +                   Sizing Parameters                                                                           1 "Chemical"                                                                            1 Resistance to                                                                         1 Chemical                                                                           1 Chemical                                                                            1 Chemical                                                                            1 Strand                    Involved     resistance                                                                              mechanical abuse                                                                        resistance                                                                           resistance                                                                            resistance                                                                            filamentation                                     (impact action)                                                       2 Resistance to         2 Resistance                                                                          2 Resistance                                                                          2 Strand-matrix                          mechanical abuse        to mechanical                                                                         to mechanical                                                                         "bonding"                                (shearing action)       abuse (tumble                                                                         abuse (tumble                                                           action)                                                                               action)                            __________________________________________________________________________

Wet integrity determinations were made by means of a slump procedure. The wet integrity properties reflect the size compositions' ability to withstand mechanical abuse and chemical attack by a high pH, abrasive aqueous medium. This procedure involves mixing 1% of 1/2" chopped strands into a cement-sand-water slurry for three minutes. A cone is filled with the slurry, inverted and removed. The water content of the control is adjusted to give a slump of about 25% of the original height of the cone. Slumps of the samples are then expressed as the ratio of measured slump divided by the slump of the control determined the same day. All variables were the same except for the size composition. Our results indicated that the wet integrity of the sized strands of this invention were about equivalent to the control.

Wet integrity determinations by means of measurements of the extent of filamentation were also made in the laboratory. A mix similar to the one used for the slump procedure was subjected to mixing periods of up to 30 minutes. Every three minutes a small sample was removed and through careful rinsing on a screen the glass fibers were separated. The dried fibers were then compared with a similar set obtained for the control. These results indicated that under prolonged mixing conditions the wet integrity of the sized strand of this invention was better than that of the control.

We made dry integrity determinations by the following procedure. This procedure involves mixing 4% of 1/2" chopped strands into dry cement and recording the mixing times needed to give 50% filamentation. Being a dry mix of cement and chopped strands, the test gives a measure of the strands' ability to withstand mechanical abuse. The dry integrity of strands sized with these compositions were especially good. The mixing times for the sized strands of this invention were about four times greater than the control.

The chemical resistance basically involves a strand exposure to a high pH aqueous medium. Sized strands are exposed to aqueous solutions of saturated calcium hydroxide (Ca(OH)₂), 1% sodium hydroxide (NaOH), and 1% potassium hydroxide (KOH) for 48 hours. The extent of filamentation then is recorded and compared. The evaluation indicates that the sizes of this invention have greater chemical resistance to high pH media than the control.

Workability and strand integrity measurements were made for concrete mixes containing one inch chopped strands. During these evaluations small portions of the mix were taken following each mixing period. Through water rinsing, the glass fibers were separated from the matrix and dried for visual record of strand breakdown. The procedure we followed includes mixing Portland cement, No. 8 gravel, sand, water, and glass fibers in a concrete mixer. The water/cement ratio was 0.55 and the volume of glass fibers was 1.0%. The water, cement, gravel, and sand were placed into the mixer while the mixer was operating, and glass fibers were added over a one-minute period and then mixed for one more full minute. Slump as previously described was measured. The mix continued for three more minutes followed by slump determinations. The three-minute procedure was followed twice more for a total mixing time of all ingredients of ten minutes. The visual observations and slump measurements taken every three minutes indicate that the new sizes are improvements over the control in terms of workability and filamentation rating. We obtained our concrete beam properties by casting beams after the four-minute and ten-minute mixing times from the previous concrete mixing. These samples were made large enough for such castings. The beams were aged for 28 days at room temperature and tested for various physical properties such as compressive and flexural strength. The physical properties for the beams made with the sized strands of this invention represent no significant change from the control.

On forming and run-out evaluations, the size compositions of this invention gave acceptable levels of strand solids with good run-out. The strands of this invention gave less break-out in the creel during the chopping operation. These properties represent an improvement over the control.

While this invention has been described with reference to the use of an acrylate-vinyl acetate copolymer, it will be understood that various changes and modifications can be made in the details of material, procedure, formulation, and use without departing from the spirit of the invention, especially as defined in the following claims. 

We claim:
 1. A glass fiber strand comprising: a plurality of glass filaments that are coated at forming with an aqueous emulsion of an unplasticized film former comprising a copolymer of from 70 to 80% vinyl acetate and 20 to 30% of an acrylate ester whose ester portion contains an alkyl radical of from 2 to 8 carbon atoms, said film former comprising between 1.4 and 2.5 weight percent of the total dry strand weight, and said coated fibers being drawn together into a strand and dried, and whereby the fibers of the strand are bonded together with a high degree of strand integrity that is preserved when the strand is chopped.
 2. A coiled package of the strand of claim 1 wherein the strand when coated with the aqueous emulsion is coiled into a package before drying, and following which the coils of strand can be separated from each other without disruption of the strand.
 3. The strand of claim 2 uncoiled from the package and chopped into lengths between approximately 1/4 inch and approximately 2 inches.
 4. A cementitious material having a high alkali content and reinforced by the chopped strand of claim
 3. 